SU-8: Difference between revisions
imported>Silvan Schmid (SU-8 negative-tone photoresist for MEMS) |
imported>Subpagination Bot m (Add {{subpages}} and remove any categories (details)) |
||
| (5 intermediate revisions by 3 users not shown) | |||
| Line 1: | Line 1: | ||
{{subpages}} | |||
'''SU-8''' is an epoxy-based negative-tone [[photoresist]] for [[microelectromechanical system|microelectromechanical systems]] (MEMS). | |||
==Description== | ==Description== | ||
'''SU-8''' | '''SU-8''' was developed from IBM Research <ref>LaBianca N., Gelorme J.D., High-aspect-ratio resist for thick-film applications, Advances in Resist Technology and Processing XII (Ed. R. D. Allen), Processing SPIE, Vol. 2438, p. 846-852, 1995.</ref>. SU-8 is prepared by dissolving an EPON SU-8 resin in an organic solvent. There are two different solvents available, gamma butyrolacton (GBL) and cyclopentanone. The SU-8 dissolved with the latter solvent is called SU-8 2000. The ratio of solvent | ||
structured by placing a mask between the resist and the light source during exposure, | to EPON determines the viscosity which influences the thickness of the resist layer when spun on a substrate. | ||
SU-8 is a near-UV epoxy-based photoresist. The polymerization of SU-8 is based on chemical amplification, initiated upon UV-exposure, starting a cascade of subsequent chemical reactions. An acid is generated which catalysts the crosslinking formed among the epoxy groups. The monomers with eight epoxy sites yield a dense stable polymer. | |||
The resist is structured by placing a mask between the resist and the light source during exposure, | |||
thereby making the parts hit by light insoluble and the parts protected by the | thereby making the parts hit by light insoluble and the parts protected by the | ||
mask pattern soluble in the developer, typically PGMEA (propylene glycol methyl ether acetate). Cured SU-8 has a high chemical resistance and excellent thermal stability. SU-8 structures with very high aspect ratios (20:1) and tall thicknesses (millimeter thick) can be fabricated using standard UV contact lithography. The photoresist is well suited for [[MEMS]]/Micromachining, UV-LIGA, and other thick and ultra thick (>50 μm) applications. | mask pattern soluble in the developer, typically PGMEA (propylene glycol methyl ether acetate). Cured SU-8 has a high chemical resistance and excellent thermal stability. SU-8 structures with very high aspect ratios (20:1) and tall thicknesses (millimeter thick) can be fabricated using standard UV contact lithography. The photoresist is well suited for [[MEMS]]/Micromachining, UV-LIGA, and other thick and ultra thick (>50 μm) applications. | ||
==External Links== | ==External Links== | ||
[http://www.microchem.com SU-8 supplier]<br/> | * [http://www.microchem.com SU-8 supplier]<br/> | ||
[http://memscyclopedia.org/su8.html Free MEMS Encyclopedia] Physical properties and processing instructions<br/> | * [http://memscyclopedia.org/su8.html Free MEMS Encyclopedia] Physical properties and processing instructions<br/> | ||
[http://www.cise.columbia.edu/clean/msds/su-8resist.pdf Material Safety Data Sheet]<br/> | * [http://www.cise.columbia.edu/clean/msds/su-8resist.pdf Material Safety Data Sheet]<br/> | ||
[http://www.geocities.com/guerinlj/ A SU-8 Homepage] | * [http://www.geocities.com/guerinlj/ A SU-8 Homepage] | ||
==References== | ==References== | ||
<references /> | <references /> | ||
Latest revision as of 21:30, 14 November 2007
SU-8 is an epoxy-based negative-tone photoresist for microelectromechanical systems (MEMS).
Description
SU-8 was developed from IBM Research [1]. SU-8 is prepared by dissolving an EPON SU-8 resin in an organic solvent. There are two different solvents available, gamma butyrolacton (GBL) and cyclopentanone. The SU-8 dissolved with the latter solvent is called SU-8 2000. The ratio of solvent to EPON determines the viscosity which influences the thickness of the resist layer when spun on a substrate.
SU-8 is a near-UV epoxy-based photoresist. The polymerization of SU-8 is based on chemical amplification, initiated upon UV-exposure, starting a cascade of subsequent chemical reactions. An acid is generated which catalysts the crosslinking formed among the epoxy groups. The monomers with eight epoxy sites yield a dense stable polymer.
The resist is structured by placing a mask between the resist and the light source during exposure, thereby making the parts hit by light insoluble and the parts protected by the mask pattern soluble in the developer, typically PGMEA (propylene glycol methyl ether acetate). Cured SU-8 has a high chemical resistance and excellent thermal stability. SU-8 structures with very high aspect ratios (20:1) and tall thicknesses (millimeter thick) can be fabricated using standard UV contact lithography. The photoresist is well suited for MEMS/Micromachining, UV-LIGA, and other thick and ultra thick (>50 μm) applications.
External Links
- SU-8 supplier
- Free MEMS Encyclopedia Physical properties and processing instructions