SU-8: Difference between revisions
imported>Silvan Schmid No edit summary |
imported>Petréa Mitchell m (Big Cleanup) |
||
| Line 1: | Line 1: | ||
'''SU-8''' is an epoxy-based negative-tone [[photoresist]] for MEMS. | '''SU-8''' is an epoxy-based negative-tone [[photoresist]] for [[MEMS]]. | ||
==Description== | ==Description== | ||
| Line 12: | Line 12: | ||
==External Links== | ==External Links== | ||
[http://www.microchem.com SU-8 supplier]<br/> | * [http://www.microchem.com SU-8 supplier]<br/> | ||
[http://memscyclopedia.org/su8.html Free MEMS Encyclopedia] Physical properties and processing instructions<br/> | * [http://memscyclopedia.org/su8.html Free MEMS Encyclopedia] Physical properties and processing instructions<br/> | ||
[http://www.cise.columbia.edu/clean/msds/su-8resist.pdf Material Safety Data Sheet]<br/> | * [http://www.cise.columbia.edu/clean/msds/su-8resist.pdf Material Safety Data Sheet]<br/> | ||
[http://www.geocities.com/guerinlj/ A SU-8 Homepage] | * [http://www.geocities.com/guerinlj/ A SU-8 Homepage] | ||
==References== | ==References== | ||
| Line 21: | Line 21: | ||
[[Category:CZ Live]] | [[Category:CZ Live]] | ||
[[Category:Chemistry Workgroup]] | |||
[[Category:Visual Arts Workgroup]] | |||
Revision as of 10:57, 28 April 2007
SU-8 is an epoxy-based negative-tone photoresist for MEMS.
Description
SU-8 was developed from IBM Research [1]. SU-8 is prepared by dissolving an EPON SU-8 resin in an organic solvent. There are two different solvents available, gamma butyrolacton (GBL) and cyclopentanone. The SU-8 dissolved with the latter solvent is called SU-8 2000. The ratio of solvent to EPON determines the viscosity which influences the thickness of the resist layer when spun on a substrate.
SU-8 is a near-UV epoxy-based photoresist. The polymerization of SU-8 is based on chemical amplification, initiated upon UV-exposure, starting a cascade of subsequent chemical reactions. An acid is generated which catalysts the crosslinking formed among the epoxy groups. The monomers with eight epoxy sites yield a dense stable polymer.
The resist is structured by placing a mask between the resist and the light source during exposure, thereby making the parts hit by light insoluble and the parts protected by the mask pattern soluble in the developer, typically PGMEA (propylene glycol methyl ether acetate). Cured SU-8 has a high chemical resistance and excellent thermal stability. SU-8 structures with very high aspect ratios (20:1) and tall thicknesses (millimeter thick) can be fabricated using standard UV contact lithography. The photoresist is well suited for MEMS/Micromachining, UV-LIGA, and other thick and ultra thick (>50 μm) applications.
External Links
- SU-8 supplier
- Free MEMS Encyclopedia Physical properties and processing instructions
- Material Safety Data Sheet
- A SU-8 Homepage
References